High Translucent Plus White Zirconia Block

Strength: 1300Mpa
Transmittance: 40%
Thickness: 10-25mm
Color: White
Aging Properties: Monoclinic Phase<25%
Radioactivity: <0.02
Sintered: ≥6.06g/cm 3
Chemical
solubility:
<100µ g /m 2

High Translucent Plus White Zirconia Block

XANGTECH high translucent plus white zirconia block is one of the most commonly used materials in dental laboratories because of its hard texture, good chemical properties and excellent biocompatibility.It is cheap, high quality and manufactured under cold isostatic pressing, giving it a more uniform service life.It combines affordability with superior quality. It offers a cost-effective solution while ensuring that dental professionals provide their patients with aesthetically pleasing and durable restorations. Through our advanced cold isostatic pressing technology, we ensure that each zirconia block achieves a uniform and consistent level, thus guaranteeing consistent, reliable results for every restoration. This precise approach ensures that dental professionals can rely on the material’s consistent performance and aesthetic results. More than just a dental material, it is a testament to innovation, quality and affordability.

ht zirconia
  • High degree of stain resistance
  • Cold isostatic pressing for longer service life
  • Can be milled with high precision, contributing to improved oral function
  • High strength for those with special strength requirements
ht zirconia

Case Picture Of High Translucent Plus White Zirconia Block

XANGTECH high translucent plus white zirconia block will play an important role in improving the quality and longevity of dental restorations

  • case
  • ht zirconia block
  • ht zirconia block
  • ht zirconia block
  • case
Scroll to Top